Studium wytłaczania polietylenu z dodatkiem nanorurek haloizytowych. Cz II. Właściwości mechaniczne i przetwórcze
Loading...
Sikora_i_inni_PCh 08_2019.pdf (3.11 MB)
Date
2019-08
Journal Title
Journal ISSN
Volume Title
Publisher
Wydawnictwo Czasopism i Książek Technicznych SIGMA-NOT Sp. z o.o. ul. Ratuszowa 11, 00-950 Warszawa
Abstract
Low d. polyethylene prepd. by K. Głogowska and Ł. Majewski (2019) was studied for mech. properties (Young modulus, tensile strength) as well as processability (melt flow rate indexes and material swelling behind the extruder head). The increase in the content of halloysite in the tested materials resulted in the redn. of their Young modulus and tensile strength and in an increase of the melt flow rates. The 2% addn. of halloysite resulted in decreasing the material swelling. The increase in the swelling value was obsd. for higher additive contents and higher rotational speeds of the extruder screw.Określono wpływ parametrów wytwarzania oraz zawartości masowej nanorurek haloizytowych HNT (halloysite nanotubes) na wybrane właściwości mechaniczne oraz przetwórcze wytłoczyny z polietylenu o małej gęstości. Próbki pomiarowe wytłoczono z wykorzystaniem wytłaczarki jednoślimakowej przy zmiennej prędkości obrotowej ślimaka. Dokonano pomiarów masowego i objętościowego wskaźnika szybkości płynięcia oraz oceniono wpływ wybranych czynników zmiennych na intensywność pojawiającego się podczas wytłaczania efektu Barusa. Przeprowadzono analizę zmian podstawowych właściwości mechanicznych otrzymanych wytłoczyn na podstawie wyników ze statycznej próby rozciągania.
Description
Keywords
Citation
Sikora J. W., Majewski Ł., Głogowska K. (2019). Studium wytłaczania polietylenu z dodatkiem nanorurek haloizytowych. Cz II. Właściwości mechaniczne i przetwórcze. Przemysł Chemiczny, 98(8), 1316 - 1318. 10.15199/62.2019.8.22.