The Statistic Evaluation of the Quality of the Surface Treatments
Oglądaj/ Otwórz
Data
2013Autor
Svobodová, Jaroslava
Kuśmierczak, Sylvia
Náprstková, Nataša
Metadane
Pokaż pełny rekordStreszczenie
The article deals with evaluation of the quality of the surface treatment on the
service life of the experimental samples. We have tested two sets of samples, which was
pre-treated by the different ways. We have used one kind of material – laboratory used
material Q-panel Fe - for the experiment. The material was pre-treated by mechanical pretreatment
(soft blasting) and chemical pre-treatments (alkaline degreasing, ferric
phosphate and zirconium nanopassivation). For all samples it was measured the thickness
of the coated layer before insertion into the spray chamber at five points of the each
experimental sample and for all chemical pre-treatments was measured surface roughness.
The results are summarized in tables and graphs. Then the samples were placed in to
corrosion chamber and subjected to salt spray corrosion test. The sample loading time was
chosen according to the standard for 480, 720 and 1000 hours. The samples were
compared with each other and their status was evaluated after corrosive load in corrosion
chamber after removal from the corrosive environment. Experimental samples were
statistically evaluated according to the thickness measurement of coated layer, chemical
pre-treatment surface roughness and their effect on the corrosion resistance of painted
sheet metal.